Ultra High Gloss Clear Transparent Epoxy Resin

Epoxy resin, mixed with pigment, may be used as a painting medium, by pouring layers on top of each other to form a complete picture. It is also used in jewelry, as a doming resin for decorations and labels, and in decoupage type applications for art, countertops, and tables.

TECHNICAL SPECIFICATION

It is two-part epoxy system with High Glossy , Transparent, low viscosity and UV stable liquid epoxy resin for casting, coatings, and adhesive applications. It is a range of high-performance user-friendly epoxy resins.

FEATURES & BENEFITS:

  • 100% Clear & Transparent.
  • High Gloss Finishing Green
  • Non Yellowing
  • Can be Pigmented using suitable pigments
  • Very less shrinkage
  • Industry leading UV stability
  • Excellent moisture protection barrier, stable in acidic pH solutions
  • Excellent flow properties (low viscosity) with efficient substrate wetting
  • Unique mechanical properties

STORAGE & PRE –MIXING:

The two components ( Resin & hardener ) should be stored in separate at all times prior to use. Store in cool , Dry & Away from Sun Light.

Warm Temperature should be avoided in storage area , Warm temperature reduce the shelf life. The handling equipment & the storage area should be free from chemical residue , Foreign matters.

TECHNICAL GUIDELINES FOR USING:

  • Measure the Part A ( Resin ) and the Part B ( Hardener ) in two separate containers.
  • Transfer Part A into the suitable Glass Beak
  • Start gentle stirring
  • After stirring the part A, transfer Part B to it.
  • Continue the gentle stirring & Reaction to progress.
  • Take care not to get air trapped within mixture
  • The Mixed epoxy resin should be applied or poured within 5-10 min Time.
  • For design applications, Degassing may be required to remove the Air bubbles from the texture.
  • Upon curing remove the material from moulds.
  • SHELF LIFE:
  • Twelve (12) months from date of shipment when stored at 25ºC in the original sealed packages.

FIRST AID:

  • Eye Contact: Flush eyes with plenty of water. If irritation persists, seek medical attention.
  • Skin Contact: In case of skin contact, wash thoroughly with soap and water; remove contaminated clothing and launder before reuse; seek medical attention if rash develops.
  • Ingestion: Do not induce vomiting unless instructed by a physician. Contact physician immediately.

Ultra High Gloss Clear Transparent Epoxy Resin

ULTRA HIGH GLOSS & TRANSPARENT EPOXY RESIN - BUCR53

Sr.No DESCRIPTION PARAMETERS
RESIN HARDENER
1 Physical State Low Viscous Liquid Low Viscous Liquid
2 Colour Clear Clear
3 Viscosity (mPas 25 ºC) 1160 479
4 Mixing Ratio 100 60
5 Gel Time @ 25 ºC (Min) 5-10 min
6 Set Time (Min) 15-20 Min
7 Drying Time (Min) 30-40 Min

ULTRA HIGH GLOSS & TRANSPARENT EPOXY RESIN - BUCR2153

CAST A and CAST B  
Viscosity Part A cps 25 °C 900.00 cps
Viscosity Part B cps 25 °C 10.00 cps
Appearance A/B Clear Liquid/ Clear Liquid
Density Part A/Part B at 25 °C g/ml 1.01/0.98
Mixing Ratio A:B 100:30
Gel time in bulk at 25 °C 60-90 min
A Epoxy Equivalent weight 240 g/eq
B Active-H Equiv. Weight 72 g/eq
Tacky free at 25 °C 5-6hrs
Hardness in Shore D ASTM D 2240 5
Minimum reaction temperature +15 °C
Maximum temperature of use after hardening 60 °C

OUR PRODUCTS

Sign up for our newsletter

Vision

Innovation, Quality, Prompt Service, On time delivery.

Quality Policy

Aimed at delivering value and achieving complete customer satisfaction.

Core Strenghts

Expertise is in manufacturing high-quality products.

Contact Details
Burhani Engineering Technology

Address : 137 Linghi Chetty Street,
Mukunalla Muthu Corner, Parrys,
High court, Chennai - 600001, India.

Burhani Engineering Technolog

We Offer Proffesional Consultation For Free

For all Your Vacuum Chambers,
Vacuum Degassing Chamber, Bubble test Chamber
and Filling machine needs.

Our Location
© 2023 Burhani Engineering Technology | All Rights Reserved | Privacy Policy

Sharp Graphics